Mainly used for:materials use temperature of l 00 degrees,the alkali content一>(20%sodium hydroxide)pressure filtration and other applications requiring high tensile strength,high wear resistance of the industry.
Type | Filamentdiameter mm | Density/root Cm | N/cm Tensilestrength | weight Kg/m² | Thickness mm | Air Permrability M3/m2h | CFM 127/pa | Matenal | |||
warp | weft | warp | Weft | surface | Joint | ||||||
121104 | 0.90 | 1.1 | 12.8 | 4.0 | 1600 | 900 | 1.57 | 3.05 | 9600 | 600 | PA66 |
15905 | 0.90 | 0.90 | 15.3 | 5 | 1600 | 900 | 2.0 | 2.77 | 6800 | 425 | PA66 |
061204 | 1.2 | 1.2 | 7 | 4.3 | 1600 | 900 | 1.9 | 2.9 | 6896 | 43t | PET |